AISI 1215 Free Machining Steel Services

When production speed and surface finish are the top priorities, AISI 1215 is the undisputed champion of carbon steels. Known as "screw stock," this resulfurized and rephosphorized steel is engineered specifically for maximum machinability. It allows for cutting speeds significantly higher than standard mild steels like 1018, resulting in drastically reduced cycle times. At JUCHENG, we utilize 1215 primarily in our Swiss Turning and Automatic Lathe departments to produce high volumes of bushings, couplings, and inserts. It is the most cost-effective solution for non-structural parts that require precise dimensions and a smooth, polished look.

Laden Sie Ihre CAD-Datei hoch für ein Angebot Materialien anzeigen
AISI 1215 Free Machining Steel Services
AISI 1215 Free-Machining Steel Material
When production speed and surface finish are the top priorities, AISI 1215 is the undisputed champion of carbon steels. Known as "screw stock," this resulfurized and rephosphorized steel is engineered specifically for maximum machinability. It allows for cutting speeds significantly higher than standard mild steels like 1018, resulting in drastically reduced cycle times. At JUCHENG, we utilize 1215 primarily in our Swiss Turning and Automatic Lathe departments to produce high volumes of bushings, couplings, and inserts. It is the most cost-effective solution for non-structural parts that require precise dimensions and a smooth, polished look.
1215 legierter Stahl

JUCHENG's 1215 Machining Capabilities

We optimize our workflow to leverage the speed of 1215 for mass production:
  • Lights-Out Manufacturing: 1215 produces small, broken chips that do not clog machines. This allows our CNC lathes to run unattended 24/7 with bar feeders, maximizing throughput.
  • Überlegene Oberflächenqualität: The chemical composition of 1215 inhibits the formation of built-up edges (BUE) on tools, allowing us to achieve smooth, bright finishes directly from the machine without secondary polishing.
  • Complex Turning: We can machine intricate threads, knurls, and deep holes rapidly, making it ideal for complex fittings.
  • Plating Readiness: We offer post-machining Zinc Plating (Clear/Yellow/Black) or Black Oxide coating, which adheres excellently to the smooth surface of 1215.

Advantages of CNC Machining 1215

Vorteil Detaillierte Beschreibung Hauptvorteil
Highest Machinability Rated at ~136% machinability (compared to 1212 baseline). It cuts faster than almost any other steel. Lowest possible unit cost due to minimal machine time.
Excellent Surface Finish Cuts cleanly without tearing, leaving a satin-like smooth surface. Often eliminates the need for grinding or polishing.
Extended Tool Life The sulfur content lubricates the cut, reducing friction on cutting tools. Reduces downtime for tool changes, keeping production continuous.
Maßhaltigkeit Machines with very low vibration and cutting force. Easy to hold tight tolerances on long, slender parts.
Kosteneffizienz Combination of low material cost and fast processing. The most economical choice for fittings and fasteners.

Technische Parameter & Materialnormen

1215 is the modern, environmentally friendly replacement for leaded steels (like 12L14) in many applications:
Güteklasse Spezifikation Eigenschaften & Ideale Verwendungen
AISI / SAE 1215 Free-Machining Characteristics: Low Carbon (0.09% max), High Manganese, Sulfur, and Phosphorus. The sulfur forms manganese sulfide inclusions which act as chip breakers.
Uses: Bushings, inserts, coupling parts, hydraulic fittings, pins, screws.
EN 1.0736 11SMn37 Characteristics: The European equivalent. Offers identical high-speed machining performance.
Uses: High-volume turned parts for automotive and general industry.

CNC Machining Guidelines 1215

  • Schweißen: Do Not Weld. The high sulfur and phosphorus content causes porosity and hot cracking. Parts must be assembled via threads or press-fits.
  • Festigkeit: 1215 has relatively low tensile strength and ductility compared to 1018. It should not be used for components subjected to high fatigue, shock, or structural loads.
  • Korrosion: It has poor corrosion resistance and will rust quickly. A protective coating (Zinc Plate, Nickel, or Oil) is mandatory for final parts.
  • Einsatzhärtung: While it cannot be through-hardened, it can be case-hardened (carburized) to improve surface wear resistance, though the core remains soft.

Anwendungsszenarien

  • Automobil: Fluid connectors, brake pins, sensor housings, spacers.
  • Industrie: Hydraulic fittings, hose crimp collars, conveyor rollers.
  • Befestigungselemente: Custom bolts, nuts, studs, standoffs.
  • Elektronik: Mounting hardware, knurled thumb screws.
  • Möbel: Dowel pins, assembly cam locks.

Tabelle der physikalischen Eigenschaften

Comparison: 1215 (Free Machining) vs 1018 (Standard Mild):
Eigenschaft AISI 1215 AISI 1018 Einheit
Zerspanbarkeit 136% 78% Bewertung
Zugfestigkeit 380 - 540 440 MPa
Streckgrenze 225 - 415 370 MPa
Härte (Brinell) 121 126 HB
Dehnung 10 - 13% 15% (Lower ductility)
Schweißbarkeit Schlecht Hervorragend -
 
Jucheng Precision Factory
Fordern Sie Ihr DFM & Angebot an – Laden Sie Ihre Zeichnungen hoch
ㆍGeben Sie Ihre Anforderungen ein und laden Sie Ihre 2D- und 3D-Dateien hoch. Wir senden Ihnen innerhalb von 24 Stunden Ihr Projektangebot und DFM zurück.
ㆍDateitypen: STEP, STP, IGES, IGS, SLDPRT, 3DM, SAT, X_T, DWG, DXF, STL, PDF, ZIP und mehr. Dateigröße: < 128 MB Teilegröße: < 1500*1500*1500 mm
ㆍDatenschutz: Wir respektieren Ihre Privatsphäre. Hier finden Sie ein Beispiel einer Geheimhaltungsvereinbarung. Mit dem Absenden dieses Formulars stimmen Sie unseren AGB und der Datenschutzerklärung zu.
Datei auswählen